碳二亚胺联合不同粘接技术对牙本质粘接性能的影响

doi:10.19439/j.sjos.2022.01.010

上海口腔医学 ›› 2022, Vol. 31 ›› Issue (1): 48-53.doi: 10.19439/j.sjos.2022.01.010

碳二亚胺联合不同粘接技术对牙本质粘接性能的影响

陈月¹, 鄢国伟^1,2, 郑月梅¹, 周凯璇¹, 谢翠柳^1,3

1.西南医科大学口颌面修复重建与再生实验室,四川泸州 646000;
2.西南医科大学附属口腔医院牙体牙髓病科, 3.口腔修复科,四川泸州 646000

收稿日期:2020-04-21 修回日期:2020-06-28 出版日期:2022-02-25 发布日期:2022-03-10
通讯作者: 谢翠柳,E-mail: xiecl10@163.com
作者简介:陈月（1998-）,女,研究生, E-mail:2916067367@qq.com
基金资助:
西南医科大学青年科研项目（2019ZQN133）; 西南医科大学附属口腔医院青年科研项目（201806）

Effects of carboidiimide with different bonding techniques on the property of dentin bonding

CHEN Yue¹, YAN Guo-wei^1,2, ZHENG Yue-mei¹, ZHOU Kai-xuan¹, XIE Cui-liu^1,3

1. Oral & Maxillofacial Reconstruction and Regeneration Laboratory, Southwest Medical University. Luzhou 646000;
2. Department of Endodontics, 3. Department of Prosthodontics, the Affiliated Stomatology Hospital of Southwest Medical University. Luzhou 646000, Sichuan Province, China

Received:2020-04-21 Revised:2020-06-28 Online:2022-02-25 Published:2022-03-10

摘要/Abstract

摘要： 目的: 探讨碳二亚胺（EDC）联合不同粘接技术对牙本质粘接性能的影响。方法: 取离体第三磨牙64颗,随机分为8组(n=8)：EWB和EWBa(无预处理+乙醇湿粘接)、E-EWB和E-EWBa(0.5 mol/L EDC+乙醇湿粘接)、E-WB和E-WBa(0.5 mol/L EDC+湿粘接)、E-DB和E-DBa(0.5 mol/L EDC+干粘接),其中,EWB、E-EWB、E-WB、E-DB为即刻组,EWBa、E-EWBa、E-WBa、E-DBa为老化组。每组6个试件,测试剪切强度,观察、记录断裂模式,剩余2个试件电镜下观察粘接界面。采用SPSS 20.0软件包对数据进行统计学分析。结果: 剪切强度在EWB组和E-EWB组、E-EWB组和E-WB组间差异无统计学意义(P>0.05),E-EWB组、E-WB组大于E-DB组,差异有统计学意义(P<0.05);E-EWBa组大于EWBa组,差异有统计学意义(P<0.05),E-EWBa组、E-WBa组和E-DBa组剪切强度递减,差异有统计学意义(P<0.05)。EDC、粘接技术和老化主效应的影响均有统计学意义(P<0.05),老化因素与EDC、粘接技术之间的交互效应均有统计学意义(P<0.05)。乙醇湿粘接和湿粘接的断裂模式以树脂破坏、粘接界面破坏和混合破坏为主,干粘接以粘接界面破坏为主。扫描电镜下E-EWB组混合层最厚且致密,EWBa组、E-EWBa组混合层与粘接剂之间有微小裂隙,E-WBa组混合层内可见部分不均匀裂缝,E-DBa组中混合层裂缝明显。结论: EDC联合乙醇湿粘接获得最高剪切强度且具有粘接耐久性。

关键词: 碳二亚胺, 粘接技术, 牙本质, 剪切强度

Abstract: PURPOSE: To explore the effects of carbodiimide combined with different bonding techniques on the property of dentin bonding. METHODS: 64 third molars in vitro were randomly divided into 8 groups(n=8), including EWB and EWBa (no pretreatment+ethanol-wet bonding), E-EWB and E-EWBa (0.5 mol/L EDC+ethanol-wet bonding), E-WB and E-WBa (0.5 mol/L EDC+water-wet bonding), E-DB and E-Dba (0.5 mol/L EDC+dry bonding). Group EWB, E-EWB, E-WB and E-DB were immediate groups, while group EWBa, E-EWBa, E-WBa and E-DBa were aging groups. Six specimens in each group were randomly chosen to test shear bonding strength and then observe failure patterns. The remaining specimens were used to observe bonding interface under SEM. SPSS 20.0 software package was used for statistical analysis of the data. RESULTS: There was no significant difference in shear bonding strength between group EWB and E-EWB, group E-EWB and E-WB(P>0.05), while shear bounding strength in group E-EWB and E-WB were significantly greater than group E-DB(P<0.05). The shear bonding strength of group E-EWBa was significantly greater than group EWBa (P<0.05). The shear bonding strength of group E-EWBa, E-WBa and E-DBa was gradually decreased, and their differences were significant (P<0.05). The factors of EDC, bonding techniques and aging played a significant role in shear bonding strength (P<0.05). Interactions between EDC and aging was significant (P<0.05), and that between bonding techniques and aging was also significant (P<0.05). The main failure modes of the water-wet bonding and the ethanol-wet bonding were resin failure, adhesive interface failure and mixed failure. The main failure of dry bonding was adhesive interface failure. The thickest and densest hybrid layer were found in group E-EWB. Some tiny cracks were presented between the hybrid layer and adhesives layer in group EWBa and E-EWBa. Partially uneven cracks existed in the hybrid layer in group E-WBa, and that was more obvious in group E-DBa. CONCLUSIONS: EDC pretreatment combined with ethanol-wet adhesive technique acquires the optimal shear bonding strength and the durability of dentin bonding.

Key words: 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide, Adhesive technology, Dentine, Shear bonding strength

中图分类号:

R781.05

陈月, 鄢国伟, 郑月梅, 周凯璇, 谢翠柳. 碳二亚胺联合不同粘接技术对牙本质粘接性能的影响[J]. 上海口腔医学, 2022, 31(1): 48-53.

CHEN Yue, YAN Guo-wei, ZHENG Yue-mei, ZHOU Kai-xuan, XIE Cui-liu. Effects of carboidiimide with different bonding techniques on the property of dentin bonding[J]. Shanghai Journal of Stomatology, 2022, 31(1): 48-53.

参考文献

[1] 李晓东. 牙本质粘接持久性的研究现状及思考[J]. 口腔材料器械杂志, 2019, 28(4): 181-190.
[2] Zhou J, Chiba A, Scheffel DL, et al.Cross-linked dry bonding: a new etch-and-rinse technique[J]. Dent Mater, 2016, 32(9): 1124-1132.
[3] Pashley DH, Tay FR, Carvalho RM, et al.From dry bonding to water-wet bonding to ethanol-wet bonding. a review of the interactions between dentin matrix and solvated resins using a macromodel of the hybrid layer[J]. Am J Dent, 2007, 20(1): 7-20.
[4] Yi L, Yu J, Han L, et al.Combination of baicalein and ethanol-wet-bonding improves dentin bonding durability[J]. J Dent, 2019, 90: 103207.
[5] Orellana N, Ramirez R, Roig M, et al.Comparative study of the microtensile bond strength of three different total etch adhesives with different solvents to wet and dry dentin (in vitro test)[J]. Acta Odontol Latinoam, 2009, 22(1): 47-56.
[6] Ayar MK.A review of ethanol wet-bonding: principles and techniques[J]. Eur J Dent, 2016, 10(1): 155-159.
[7] Souza MY, DI Nicoló R, Bresciani E.Influence of ethanol-wet dentin, adhesive mode of application, and aging on bond strength of universal adhesive[J]. Braz Oral Res, 2018, 32: e102.
[8] Talungchit S, Jessop JL, Cobb DS, et al.Ethanol-wet bonding and chlorhexidine improve resin-dentin bond durability: quantitative analysis using raman spectroscopy[J]. J Adhes Dent, 2014, 16(5): 441-450.
[9] Ryou H, Turco G, Breschi L, et al.On the stiffness of demineralized dentin matrices[J]. Dent Mater, 2016, 32(2): 161-170.
[10] Cadenaro M, Fontanive L, Navarra CO, et al.Effect of carboidiimide on thermal denaturation temperature of dentin collagen[J]. Dent Mater, 2016, 32(4): 492-498.
[11] Singh P, Nagpal R, Singh UP, et al.Effect of carbodiimide on the structural stability of resin/dentin interface[J]. J Conserv Dent, 2016, 19(6): 501-509.
[12] Mazzoni A, Angeloni V, Apolonio FM, et al.Effect of carbodiimide(EDC) on the bond stability of etch-and-rinse adhesive systems[J]. Dent Mater, 2013, 29(10): 1040-1047.
[13] 唐琳, 张一, 李皓, 等. 不同浓度的碳二亚胺乙醇溶液处理对牙本质自酸蚀粘接剂粘接强度的影响[J].北京大学学报(医学版),2017, 49(6): 1055-1059.
[14] Singh P, Nagpal R, Singh UP.Effect of dentin biomodifiers on the immediate and long-term bond strengths of a simplified etch and rinse adhesive to dentin[J]. Restor Dent Endod, 2017, 42(3): 188-199.
[15] Tang L, Zhang Y, Liu Y, et al.Influence of EDC on dentin-resin shear bond strength and demineralized dentin thermal properties[J]. Materials (Basel), 2016, 9(11): 1055-1059.
[16] 王丹杨, 张凌, 李芳, 等. 参与不同牙本质粘接界面退变过程中基质金属蛋白酶种类的研究[J]. 华西口腔医学杂志, 2014, 32(4): 394-399.
[17] 李木子, 甘抗, 刘秀菊, 等. 乙醇湿粘接对牙本质粘结强度及耐久性影响的研究现状[J]. 口腔医学研究, 2015, 31(3): 308-309, 312.
[18] 魏裕, 李彦. 乙醇湿粘接技术对髓腔牙本质粘接效果的影响[J].临床口腔医学杂志, 2017, 33(4): 199-203.
[19] Kuhn E, Farhat P, Teitelbaum AP, et al.Ethanol-wet bonding technique: clinical versus laboratory findings[J]. Dent Mater, 2015, 31(9): 1030-1037.
[20] Bedran-Russo AK, Vidal CM, Dos E-WBantos PH, et al. Long-term effect of carbodiimide on dentin matrix and resin-dentin bonds[J]. J Biomed Mater Res B Appl Biomater, 2010, 94(1): 250-255.
[21] Li Y, Carrera C, Chen R, et al.Degradation in the dentin-composite interface subjected to multi-species biofilm challenges[J]. Acta Biomater, 2014, 10(1): 375-383.
[22] 王霞,魏清,刘红,等.乙醇润湿对2种全酸蚀粘接剂粘接性能的影响[J].中华老年口腔医学杂志, 2016, 32(4): 394-399.

碳二亚胺联合不同粘接技术对牙本质粘接性能的影响

Effects of carboidiimide with different bonding techniques on the property of dentin bonding

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	李宗谕, 李晓琳, 尉鹏功, 曲柳, 仇丽鸿, 于雅琼. 白藜芦醇在人牙髓干细胞成牙本质向分化中的调控机制研究[J]. 上海口腔医学, 2023, 32(2): 132-136.
[2]	李莉, 谭军艳, 陈文彬, 汪隼, 王玉波. 储存条件对离体牛牙釉质粘接剪切强度的影响[J]. 上海口腔医学, 2023, 32(2): 143-146.
[3]	张斌, 贾明玉, 樊睿, 田剑刚, 葛学军, 黄瑞哲. 新型往复运动单支锉根管预备对牙本质微裂的影响[J]. 上海口腔医学, 2023, 32(1): 1-5.
[4]	毛新霞, 林晓炜, 魏轩, 李琴. 自体牙本质颗粒与Bio-Oss骨粉植入引导骨再生治疗牙周骨缺损效果比较[J]. 上海口腔医学, 2022, 31(5): 530-534.
[5]	谢惠兰, 陈江, 曹白雨, 林毅. 负载氯己定的埃洛石纳米管对牙本质粘结强度的影响[J]. 上海口腔医学, 2022, 31(5): 471-475.
[6]	黄文青, 李羽, 杨健. 不同预处理方法对龋齿牙本质微渗漏和粘结效果的影响[J]. 上海口腔医学, 2021, 30(6): 585-588.
[7]	周凯璇, 谢翠柳, 陈月, 郑月梅, 鄢国伟. 含不同溶剂的碳二亚胺对丙酮基酸蚀冲洗粘接系统粘接性能的影响[J]. 上海口腔医学, 2021, 30(5): 488-492.
[8]	李静, 张艺, 王金华. 骨形态发生蛋白-2、-4、-6、-7和-9差异性介导永生化成牙本质细胞成骨分化[J]. 上海口腔医学, 2020, 29(3): 242-249.
[9]	吴峥嵘, 左园林, 李朝晖. 自体牙本质颗粒结合富血小板纤维蛋白膜治疗93例下颌第一磨牙根分叉病变效果评价[J]. 上海口腔医学, 2020, 29(2): 213-216.
[10]	汤玉红, 徐睿, 朱倩, 冉幸. 3种镍钛器械预备重度弯曲根管后牙本质微裂纹的观察[J]. 上海口腔医学, 2019, 28(6): 581-585.
[11]	汪嘉，何智妍，冉淑君，朱来宽. 耐氟变形链球菌对树脂-牙本质粘接强度的影响[J]. 上海口腔医学, 2018, 27(3): 239-243.
[12]	汪轶, 何宏. Hybrid-coat联合树脂充填治疗敏感型楔状缺损的临床疗效观察[J]. 上海口腔医学, 2018, 27(1): 89-92.
[13]	杜建新, 胡玮. Krüpple样因子5在成牙本质细胞中的表达及临床意义[J]. 上海口腔医学, 2017, 26(6): 582-585.
[14]	万里扬, 朱洪水. 热碱溶液蚀刻对氧化锆与树脂粘接强度的影响[J]. 上海口腔医学, 2017, 26(6): 590-593.
[15]	包丽荣, 赵文青, 林田, 陆彦玲, 吴煜. BMP-2诱导人牙髓细胞分化过程中miRNA表达谱的变化[J]. 上海口腔医学, 2017, 26(5): 476-483.