Preliminary study of bonding strength between diatomite-based dental ceramic and veneering porcelains

Abstract

Abstract: PURPOSE: In order to choose the best veneering porcelain for diatomite-based dental ceramic substrate, the bonding strength between diatomite-based dental ceramics and veneering porcelains was measured, and the microstructure and elements distribution of interface were analyzed. METHODS: The coefficient of thermal expansion (CTE) of diatomite-based dental ceramics was detected by dilatometry. Three veneering porcelain materials were selected with the best CTE matching including alumina veneering porcelain (group A), titanium porcelain veneering porcelain (group B), and E-max veneering porcelain (group C). Shear bonding strength was detected. SEM and EDS were used to observe the interface microstructure and element distribution. Statistical analysis was performed using SPSS 17.0 software package. RESULTS: The CTE of diatomite-based dental ceramics at 25-500℃ was 8.85×10^-6K^-1. The diatomite-based substrate ceramics combined best with group C. Shear bonding strength between group A and C and group B and C both showed significant differences(P<0.05). SEM and EDS showed that the interface of group C sintered tightly and elements permeated on both sides of the interface. CONCLUSIONS: The diatomite-based substrate ceramics combines better with E-max porcelain veneer.

Key words: Diatomite, Veneering porcelain, Matching, Shear bonding strength

CLC Number:

R783.3

LU Xiao-li,GAO Mei-qin,CHENG Yu-ye,ZHANG Fei-min. Preliminary study of bonding strength between diatomite-based dental ceramic and veneering porcelains[J]. Shanghai Journal of Stomatology, 2015, 24(2): 177-181.

References

[1] Vichi A, Louca C, Corciolani G, et al. Color related to ceramic and zirconia restorations: a review [J]. Dent Mater, 2011, 27(1): 97-108.
[2] Beuer F, Schweiger J, Eichberger M, et al. High-strength CAD/CAM-fabricated veneering material sintered to zirconia copings-a new fabrication mode for all-ceramic restorations [J]. Dent Mater, 2009, 25(1): 121-128.
[3] Dündar M, Özcan M, Gökçe B, et al. Comparison of two bond strength testing methodologies for bilayered all-ceramics [J]. Dent Mater, 2007, 23(5): 630-636.
[4] Toygar ME, Toparli M, Sen F, et al. Fracture energy determination and critical crack propagation between core and veneer ceramic interface by experiment and finite element method [J]. Mater Des, 2009, 30(6): 2278-2282.
[5] Rocha EP, Anchieta RB, Freitas AC Jr, et al. Mechanical behavior of ceramic veneer in zirconia-based restorations: a 3- dimensional finite element analysis using microcomputed tomography data [J]. J Prosthet Dent, 2011, 105(1): 14-20.
[6] Lu XL, Xia Y, Liu M, et al. Improved performance of diatomite-based dental nanocomposite ceramics using layer-by-layer assembly [J]. Int J Nanomedicine, 2012, 7: 2153-2164.
[7] 高燕, 张富强, 何帆. 稀土氧化物着色钇稳定四方多晶氧化锆陶瓷与饰面瓷匹配性的研究 [J]. 上海口腔医学, 2011, 20(5): 486-489.
[8] Isgrò G, Kleverlaan CJ, Wang H, et al. The influence of multiple firing on thermal contraction of ceramic materials used for the fabrication of layered all-ceramic dental restorations [J]. Dent Mater, 2005, 21(6): 557-564.
[9] DeHoff PH, Barrett AA, Lee RB, et al. Thermal compatibility of dental ceramic systems using cylindrical and spherical geometries[J]. Dent Mater, 2008, 24(6): 744-752.
[10] Fischer J, Stawarzcyk B, Trottmann A, et al. Impact of thermal misfit on shear strength of veneering ceramic/zirconia composites[J]. Dent Mater, 2009, 25(4): 419-423.
[11] Fleming GJ, Dickens M, Thomas LJ, et al. The in vitro failure of all-ceramic crowns and the connector area of fixed partial dentures using bilayered ceramic specimens: the influence of core to dentin thickness ratio [J]. Dent Mater, 2006, 22(8): 771-777.
[12] Smith TB, Kelly JR, Tesk JA. In vitro fracture behavior of ceramic and metal-ceramic restorations [J]. J Prosthodont, 1994, 3(3): 138-144.
[13] Al-Dohan HM, Yaman P, Dennison JB, et al. Shear strength of core-veneer interface in bi-layered ceramics [J]. J Prosthet Dent, 2004, 91(4): 349-355.