Abstract: PURPOSE: To determine the effect of the thickness of reinforced glass ceramics on the degree of conversion (DC) of three dual-cure resin cements (Multilink N, RelyX Ultimate and NX3-Nexus). METHODS: Upcera reinforced glass ceramics and IPS e.max CAD test specimen were processed, with different thickness, transmittance was tested by ultraviolet and visible spectrometer. The DC was evaluated using Fourier transform infrared (FT-IR) spectrometer, then the degree of conversion of polymerization before and after curing was calculated. SPSS 21.0 software package was used for data analysis. RESULTS: Transmittance decreased along with the thickness of reinforced glass ceramics increased. At 2 mm -thickness transmittance of upcera lithium disilicate glass ceramics was superior to IPS e.max CAD. The DC of dual-cured resin cement was decreased with the increase of thickness. At the same 2 mm group, the DC of Multilink N and RelyX Ultimate under upcera lithium disilicate glass ceramics were superior to that under IPS e.max CAD groups. CONCLUSIONS: At 2 mm-thickness transmittance of upcera lithium disilicate glass ceramics was superior to IPS e.max CAD. At the same 2 mm group, the DC of Multilink N and RelyX Ultimate under upcera lithium disilicate glass ceramics were superior to that under IPS e.max CAD groups.

Key words: Reinforced glass ceramics, Resin cement, Degree of conversion