耐氟变形链球菌对树脂-牙本质粘接强度的影响

doi:10.19439/j.sjos.2018.02.004

上海口腔医学 ›› 2018, Vol. 27 ›› Issue (3): 239-243.doi: 10.19439/j.sjos.2018.02.004

耐氟变形链球菌对树脂-牙本质粘接强度的影响

汪嘉，何智妍，冉淑君，朱来宽

上海交通大学医学院附属第九人民医院·口腔医学院牙体牙髓病科，国家口腔医学疾病临床研究中心，上海市口腔医学重点实验室，上海市口腔医学研究所，上海 200011

收稿日期:2017-09-07 修回日期:2017-11-16 出版日期:2018-07-20 发布日期:2018-07-20
通讯作者: 朱来宽，E-mail：zhulk1997@163.com
作者简介:汪嘉（1986-），女，博士，主治医师，E-mail：tangelwj@163.com
基金资助:
中华口腔医学会牙科粘接技术临床研究青年医师专项（CSA-B2015-02）

Effect of fluoride-resistant strains of Streptococcus mutans on the bonding strength of dental resin composite

WANG Jia, HE Zhi-yan, RAN Shu-jun, ZHU Lai-kuan.

Department of Endodontics and Operative Dentistry, Shanghai Ninth People's Hospital, College of Stomatology, Shanghai Jiao Tong University School of Medicine; National Clinical Research Center of Stomatology; Shanghai Key Laboratory of Stomatology & Shanghai Research Institute of Stomatology. Shanghai 200011, China

Received:2017-09-07 Revised:2017-11-16 Online:2018-07-20 Published:2018-07-20

摘要/Abstract

摘要： 目的： 探讨耐氟变形链球菌对树脂牙本质粘接强度的影响。方法： 诱导培养耐氟变形链球菌UA159-FR及其亲代菌株UA159，选用复合树脂Z350和自酸蚀粘接剂Single bond Universal，制备牙本质-树脂复合体试件。将试件分为4组，分别浸入UA159-FR菌液、UA159菌液、BHI培养基、PBS中孵育14 d，每48 h换液1次，之后进行推出试验，检测试件粘接强度的变化。扫描电镜下观察4组粘接断面的情况。采用SPSS18.0软件包对数据进行统计学分析。结果： 在UA159-FR和UA159侵袭下，牙本质-复合树脂粘接强度显著降低，组间无显著差异。粘接界面多为混合破坏，扫描电镜下可见大量的树脂突及部分粘接面破坏。结论： 耐氟变形链球菌可破坏复合树脂粘接界面，引起粘接强度下降，破坏程度在短期内与亲代菌株无显著差异。

关键词: 牙本质-树脂复合体, 变形链球菌耐氟菌株, 变形链球菌, 粘接强度

Abstract: PURPOSE: The aim of this study was to determine the influence of fluoride-resistant strains of S. mutans on the bonding strength of dental resin composite. METHODS: Standardized specimens of resin composite (Z350), and self-etch adhesives (Single bond Universal, 3M) were incubated with S. mutans UA159, fluoride-resistant strains of S. mutans UA159 (UA159-FR) or uninoculated culture medium (Control) or PBS for up to 14 days. Resin-dentin bonded disks were subjected to push-out test. Fractured surface analysis of the specimens was performed by scanning electron microscopy(SEM). SPSS18.0 software package was used for statistical analysis. RESULTS: UA159-FR and UA159 were shown to decrease the bond strengths in levels comparable with those found in the control groups (P<0.05). SEM confirmed the increased degradation of all materials with UA159-FR and UA159, compared with control and PBS. CONCLUSIONS: The results suggest that resin-dentin interface can be compromised by oral bacteria that contribute to the progress of secondary caries. Fluoride-resistant strains of S. mutans and its parental strains both decrease bonding strengths in a short time, but no significant difference in the extent of damage.

Key words: Dental resin composite, Fluoride-resistant Streptococcus mutans, Streptococcus mutans, Bond strengths

中图分类号:

R781.3

汪嘉，何智妍，冉淑君，朱来宽. 耐氟变形链球菌对树脂-牙本质粘接强度的影响[J]. 上海口腔医学, 2018, 27(3): 239-243.

WANG Jia, HE Zhi-yan, RAN Shu-jun, ZHU Lai-kuan.. Effect of fluoride-resistant strains of Streptococcus mutans on the bonding strength of dental resin composite[J]. Shanghai Journal of Stomatology, 2018, 27(3): 239-243.

参考文献

[1] Beazoglou T, Eklund S, Heffley D, et al. Economic impact of regulating the use of amalgam restorations [J]. Public Health Rep, 2007, 122(5): 657-663.
[2] Spencer P, Ye Q, Misra A, et al. Proteins, pathogens, and failure at the composite-tooth interface [J]. J Dent Res, 2014, 93(12): 1243-1249.
[3] Mj?r IA. Clinical diagnosis of recurrent caries [J]. J Am Dent Assoc, 2005, 136(10): 1426-1433.
[4] Opdam NJ, Bronkhorst EM, Roeters JM, et al. A retrospective clinical study on longevity of posterior composite and amalgam restorations [J]. Dent Mater, 2007, 23(1): 2-8.
[5] Beyth N, Domb AJ, Weiss EI. An in vitro quantitative antibacterial analysis of amalgam and composite resins [J]. J Dent, 2007, 35(3): 201-206
[6] Montanaro L, Campoccia D, Rizzi S, et al. Evaluation of bacterial adhesion of Streptococcus mutans on dental restorative materials [J]. Biomaterials, 2004, 25(18): 4457-4463.
[7] Beyth N, Bahir R, Matalon S, et al. Streptococcus mutans biofilm changes surface-topography of resin composites [J]. Dent Mater, 2008, 24(6): 732-736.
[8] ten Cate JM. Biofilms, a new approach to the microbiology of dental plaque [J]. Odontology, 2006, 94(1): 1-9
[9] 姜葳. 变异链球菌压力耐受机制的研究进展 [J]. 国际口腔医学杂志, 2011, 38(1): 44-47.
[10] 梁景平. 牙菌斑生物膜特性研究进展 [J]. 上海交通大学学报(医学版), 2007, 27(2):123-127.
[11] Deligeorgi V, Mjor IA, Wilson NH. An overview of reasons for the placement and replacement of restorations[J]. Prim Dent Care, 2001, 8(1): 5-11.
[12] De Munck J, Van Landuyt K, Peumans M, et al. A critical review of the durability of adhesion to tooth tissue: methods and results[J]. J Dent Res, 2005, 84(2): 118-132.
[13] Koshiro K, Inoue S, Sano H, et al. In vivo degradation of resin-dentin bonds produced by a self-etch and an etch-and-rinse adhesive [J]. Eur J Oral Sci, 2005, 113(4): 341-348.
[14] Caixeta RV, Guiraldo RD, Kaneshima EN, et al. Push-out bond strength of restorations with bulk-fill, flow, and conventional resin composites [J]. Sci World J, 2015, 2015: 452976.
[15] Li Y, Carrera C, Chen R, et al. Degradation in the dentin-composite interface subjected to multi-species biofilm challenges [J]. Acta Biomater, 2014, 10(1): 375-383.
[16] Segreto D, Brandt WC, Correr-Sobrinho L, et al. Influence of irradiance on the push-out bond strength of composite restorations photoactivated by LED[J]. J Contemp Dent Pract, 2008, 9(2): 89-96.
[17] 孙喆, 梁景平, 张岚. 声波器械去除根管玷污层能力的比较研究 [J]. 牙体牙髓牙周病学杂志, 2005, 15(7): 382-386.
[18] McBain AJ. Chapter 4: In vitro biofilm models: an overview [J]. Adv Appl Microbiol, 2009, 69: 99-132.
[19] Ferracane JL. Models of caries formation around dental composite restorations [J]. J Dent Res, 2017, 96(4): 364-371.
[20] Bourbia M, Ma D, Cvitkovitch DG, et al. Cariogenic bacteria degrade dental resin composites and adhesives [J]. J Dent Res, 2013, 92(11): 989-994.
[21] 盛江筠, 刘正. 变形链球菌耐氟菌株的诱导及产酸性的实验研究 [J]. 中华口腔医学杂志, 2000, 35(2): 95-98.
[22] Lenzi TL, Calvo AF, Tedesco TK, et al. Effect of method of caries induction on aged resin-dentin bond of primary teeth [J]. BMC Oral Health, 2015, 15: 79.
[23] 许华, 刘英群. 变异链球菌耐氟菌株的致龋能力 [J]. 国际口腔医学杂志, 2013, 40(5): 698-700.
[24] Zhang N, Ma YS, Weir MD, et al. Current Insights into the modulation of oral bacterial degradation of dental polymeric restorative materials [J]. Materials (Basel), 2017, 10(5): E507.

耐氟变形链球菌对树脂-牙本质粘接强度的影响

Effect of fluoride-resistant strains of Streptococcus mutans on the bonding strength of dental resin composite

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 9

编辑推荐

Metrics

本文评价

[1]	朱红, 魏萌, 刘攀, 袁璐, 张研楠, 陈剑锋. 不同频率铒激光对氧化锆陶瓷粘接性能的影响[J]. 上海口腔医学, 2022, 31(5): 460-465.
[2]	何智妍, 周薇, 黄正蔚, 梁景平, 姜葳. 变形链球菌luxS基因突变对口腔混合细菌生物膜的影响[J]. 上海口腔医学, 2019, 28(2): 113-117.
[3]	程竑，董聪，张富强. 摩擦化学法硅涂层对氧化锆陶瓷粘接强度的影响[J]. 上海口腔医学, 2018, 27(3): 248-251.
[4]	耿黎，乔广艳，顾凯凯. 氟对变形链球菌黏附前后纯钛表面腐蚀性能的影响[J]. 上海口腔医学, 2016, 25(2): 150-156.
[5]	李振玲, 张志民, 李朋莲, 张桐菲, 李天博, 刘富萍. ffh基因沉默对变形链球菌耐氟菌株耐酸性的影响[J]. 上海口腔医学, 2015, 24(4): 395-399.
[6]	苑克勇,马瑞,朱彩莲,李鸣宇,何智妍,周薇. 冷光美白对釉质表面细菌生物膜形成的影响[J]. 上海口腔医学, 2015, 24(3): 283-287.
[7]	孔方圆, 郑元俐, 李静. 添加纳米聚磷腈对聚氨酯材料微生物黏附性能的影响[J]. 上海口腔医学, 2014, 23(4): 419-422.
[8]	王晶, 刘建国, 姜晶, 王伟, 白国辉, 管晓燕. 防龋基因疫苗pcDNA3-PAc兔鼻腔黏膜免疫防龋的实验研究[J]. 上海口腔医学, 2014, 23(2): 133-137.
[9]	杨宁宁;何奎芳;潘乙怀;王惠宁;邓辉;麻健丰. 重组质粒pEGFP-N1-Srv+免疫SD大鼠后对龋齿的影响 [J]. 上海口腔医学, 2012, 21(6): 637-642.