填料含量和尺寸对复合树脂透明度的影响

doi:10.19439/j.sjos.2018.01.006

上海口腔医学 ›› 2018, Vol. 27 ›› Issue (1): 25-27.doi: 10.19439/j.sjos.2018.01.006

填料含量和尺寸对复合树脂透明度的影响

钱程辉, 王珏

上海市口腔病防治院,上海 200031

收稿日期:2017-10-17 修回日期:2017-11-20 出版日期:2018-02-25 发布日期:2018-03-05
通讯作者: 王珏,E-mail:wangjue1974@sina.com
作者简介:钱程辉(1980-),女,硕士,副主任医师, E-mail:qianchenghui1980@163.com

Influences of filler content and size on the translucency parameter of resin composites

QIAN Cheng-hui, WANG Jue

Shanghai Stomatological Hospital. Shanghai 200031, China

Received:2017-10-17 Revised:2017-11-20 Online:2018-02-25 Published:2018-03-05

摘要/Abstract

摘要： 目的: 研究填料大小和含量对复合树脂透明度的影响。方法: 每种颗粒大小的填料均以60%、70%、75%和80%的质量分数与基质混合,固化后制备成直径10 mm、厚度1 mm的试件,测定各组试件在标准白板(W)和金属色底板(B)上的色度值。测色系统使用CIELab系统,透明度（TP）根据公式TP=[(L*B-L*W)2+(a*B-a*W)2+(b*B-b*W)2]1/2计算。方差分析颗粒大小和含量对试件透明度的影响,采用SPSS 20.0软件包对均数进行单因素方差分析和HSD检验。结果: 不同直径填料间透明度无显著差异;当填料含量增加时,树脂试件透明度下降。结论: 当填料直径在0.7~1.5 μm范围内变化时,填料含量越高,复合树脂透明度越低。

关键词: 复合树脂, 填料含量, 填料尺寸, 透明度

Abstract: PURPOSE: The objective of this study was to investigate the influences of filler content and size on the translucency parameter of non-layered resin composites. METHODS: Three types of fillers (0.7 μm, 1.0 μm and 1.5 μm) were mixed at weight contents of 60wt%, 70wt%, 75wt%, and 80wt%. The L*, a* and b* value was analyzed based on CIELab color space of the specimen respectively on black and white background. The results of each test were analyzed with one-way ANOVA followed by Tukey's HSD test using SPSS 20.0 software package. RESULTS: For each filler size, there was a trend of decreasing translucency parameter as the filler content increased (P<0.05). The filler size did not affect the translucency parameter of the composites in this study. CONCLUSIONS: When the fillers content changed from 60wt% to 80wt%, there is a trend of decreasing translucency parameter as the filler content increased, and the filler size may not influence the translucency parameter of the composites when the size changed from 0.7 μm to 1.5 μm.

Key words: Composite resin, Filler content, Filler size, Translucency parameter

中图分类号:

R783.1

钱程辉, 王珏. 填料含量和尺寸对复合树脂透明度的影响[J]. 上海口腔医学, 2018, 27(1): 25-27.

QIAN Cheng-hui, WANG Jue. Influences of filler content and size on the translucency parameter of resin composites[J]. Shanghai Journal of Stomatology, 2018, 27(1): 25-27.

参考文献

[1] Paravina RD, Kimura M, Powers JM.Color compatibility of resin composites of identical shade designation[J]. Quintessence Int, 2006, 37(9): 713-719.
[2] Paravina RD, Westland S, Kimura M, et al.Color interaction of dental materials: blending effect of layered composites[J].Dent Mater, 2006, 22(10): 903-908.
[3] Paravina RD, Westland S, Imai FH, et al.Evaluation of blending effect of composites related to restoration size[J]. Dent Mater, 2006, 22(4): 299-307.
[4] Alharbi A, Ardu S, Bortolotto T, et al.Stain susceptibility of composite and ceramic CAD/CAM blocks versus direct resin composites with different resinous matrices[J]. Odontology, 2017, 105(2): 162-169.
[5] de Castro DT, Lepri CP, Valente ML, et al. Mechanical properties of silorane-based and methacrylate-based composite resins after artificial aging[J].Gen Dent, 2016, 64(2): 56-59.
[6] Dawson VS, Amjad S, Fransson H.Endodontic complications in teeth with vital pulps restored with composite resins: a systematic review[J]. Int Endod J, 2015, 48(7): 627-638.
[7] Awad D, Stawarczyk B, Liebermann A, et al.Translucency of esthetic dental restorative CAD/CAM materials and composite resins with respect to thickness and surface roughness[J]. J Prosthet Dent, 2015, 113(6): 534-540.
[8] Nahsan FP, Mondelli RF, Franco EB, et al.Clinical strategies for esthetic excellence in anterior tooth restorations: understanding color and composite resin selection[J]. J Appl Oral Sci, 2012, 20(2): 151-156.
[9] Paravina RD, Westland S, Johnston WM, et al.Color adjustment potential of resin composites[J]. J Dent Res, 2008, 87(5): 499-503.
[10] Cho BH, Lim YK, Lee YK.Comparison of the color of natural teeth measured by a colorimeter and shade vision system[J]. Dent Mater, 2007, 23(10): 1307-1312.
[11] Lee YK, Yu B, Lim HN.Lightness, chroma, and hue distributions of a shade guide as measured by a spectroradiometer[J].J Prosthet Dent, 2010, 104(3): 173-181.
[12] Johnston WM, Ma T, Kienle BH.Translucency parameter of colorants for maxillofacial prostheses[J].Int J Prosthodont, 1995, 8(1): 79-86.
[13] Woo ST, Yu B, Ahn JS, et al.Comparison of translucency between indirect and direct resin composites[J].J Dent, 2008, 36(8): 637-642.
[14] 孙皎. 牙科复合树脂充填修复材料的现状与趋势分析[J].口腔材料器械杂志, 2012, 21(1): 6-11.
[15] 甄风磊, 陈良, 黄从运. 牙科复合树脂中无机填料的研究进展[J]. 材料导报, 2016, 30(3): 29-32.
[16] Ferracane JL.Resin composite-state of the art[J]. Dent Mater, 2011, 27(1): 29-38.
[17] 石磊, 宋艾阳, 宫海环, 等. 纳米复合树脂研究进展[J].中国实用口腔科杂志, 2015, 8(3): 180-183.
[18] Chesterman J, Jowett A, Gallacher A, et al.Bulk-fill resin-based composite restorative materials: a review[J]. Br Dent J, 2017, 222(5): 337-344.
[19] Ausiello P, Ciaramella S, Fabianelli A, et al.Mechanical behavior of bulk direct composite versus block composite and lithium disilicate indirect Class II restorations by CAD-FEM modeling[J]. Dent Mater, 2017, 33(6): 690-701.
[20] Kawaguehi M, Fukushima T, Miyazaki K.The relationship between cure depth and transmission coefficient of visible light activated resin composites[J]. J Dent Res, 1994, 73(2): 516-521.
[21] Ruyter IE, Oysaed H.Conversion in different depths of ultraviolet and visible light activated composite resin materials[J]. Acta odontol Scand, 1982, 40(3): 179-192.

填料含量和尺寸对复合树脂透明度的影响

Influences of filler content and size on the translucency parameter of resin composites

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 13

编辑推荐

Metrics

本文评价

[1]	韩艳彦，伍甜甜，朱亚琴. 过氧化氢酶对外漂白后树脂充填体边缘微渗漏的影响[J]. 上海口腔医学, 2018, 27(3): 235-238.
[2]	孙海燕, 仇丽鸿, 杨谛. 不同激光处理60颗磨损后牙的临床疗效观察[J]. 上海口腔医学, 2017, 26(6): 619-622.
[3]	何少伟, 耿藤瑜, 孟翔峰. 流动性复合树脂核材料在短时超高光强照射下的聚合效果[J]. 上海口腔医学, 2016, 25(3): 261-265.
[4]	任强, 汪轶, 魏魁杰. 3种抛光方法修复楔状缺损的疗效评价[J]. 上海口腔医学, 2016, 25(3): 310-313.
[5]	郑沛, 陈晖. 光固化复合树脂修复术实验教学的标准化改革探讨[J]. 上海口腔医学, 2015, 24(4): 493-498.
[6]	朱铭颐,张修银. 硅烷偶联剂用量对硼酸铝晶须增强树脂挠曲强度的影响[J]. 上海口腔医学, 2015, 24(3): 294-297.
[7]	张珑,逯宜,杨柏松,郭妍,李芳萍. 不同大小MO洞型复合树脂嵌体修复应力分布的有限元分析[J]. 上海口腔医学, 2015, 24(2): 170-176.
[8]	何宏,汪轶. 3种抛光方法对2种复合树脂边缘微渗漏的影响[J]. 上海口腔医学, 2015, 24(1): 52-55.
[9]	王爽, 王青山, 张云涛, 王方辉, 王晶, 孙晓坤. 二期处理对光固化复合树脂单体转化率的影响[J]. 上海口腔医学, 2014, 23(3): 290-293.
[10]	邬雪颖, 钟群. 复合树脂高强纤维修复牙周炎患者下前牙缺失及固定松动牙[J]. 上海口腔医学, 2014, 23(2): 204-208.
[11]	龚瑜, 杨荣强, 杨红丽. 复合树脂、玻璃离子对人巨噬细胞的增殖活性和功能的影响[J]. 上海口腔医学, 2013, 22(4): 414-417.
[12]	赵蒙蒙, 王青山, 王爽, 王方辉, 舒静媛. 新型纳米羟基磷灰石复合树脂与牙本质的黏结性能评价[J]. 上海口腔医学, 2013, 22(3): 274-277.
[13]	阮丹平;吴春云;张丁华. 数字图像相关法在光固化复合树脂收缩变形测量中的应用 [J]. 上海口腔医学, 2012, 21(6): 651-655.