Abstract: PURPOSE: To explore the advantages of fiber reinforced composites veneer in repairing discolorated and defective anterior teeth. METHODS: Twenty porcelain veneers and 20 fiber reinforced composites veneers specimens of 2 cm long, 2 cm wide and 1 mm in thickness, with a longitudinal cross section of 45° incline were made. Another 40 fiber reinforced composites specimens of the same shape were used for comparison. After polishing and acid treatment of all the specimens according to clinical routine, resin cement was used for bonding the porcelain cover with resin veneers slope, and the conjunct specimens were soaked in 40 ℃ warm water for 24 h and drying; then the two groups of specimens were put were put on the pressure testing platform of the universal testing machine, with 1 mm/min testing pressure, and 1 cm² square head was contacted on the surface of the bonding interface. Computer was used to record the fracture process of the two groups of specimens and the maximum compressive strength of bonding interface automatically. The compressive strength of the bonding interface under the same conditions was evaluated. SPSS 12.0 software package was used for statistical analysis. RESULTS: The compressive strength of the bonding interface between fiber reinforced composites was significantly higher than that between porcelain and fiber reinforced composites(P<0.05). CONCLUSIONS: Compared with porcelain veneers that can not be repaired when damaged in the anterior teeth, high-strength fiber resin veneers can partially be repaired with the same material, which has obvious advantages.

Key words: Fiber reinforced composite resin veneer, Porcelain veneer, Compressive strength