Experimental research of hot alkaline solution etching treatment on zirconia/resin bonding strength

doi:10.19439/j.sjos.2017.06.004

Abstract

Abstract: PURPOSE: In this experiment, we applied hot alkaline solution (20%NaOH solutions) to treat the surfaces of zirconia ceramics in vitro, then evaluated the changes of bond strength of zirconia ceramics and resin cement. METHODS: Eighteen pieces of zirconia ceramic specimens were made, using the same method of grinding and polishing, and then randomly divided them into 3 groups: group A with hot alkali solution treatment (20%NaOH) (n=6), group B underwent sand blasting with a diameter of 110 μm alumina particles (n=6), group C was as the control group. Atomic force microscope was used to measure the roughness of the surface of the specimens, and the zirconia surfaces were scanned to get topography maps, then made them into ceramic/resin-bonded specimens. After 24 h of water reservoir processing, shearing bonding strength (SBS) test was conducted and their bond interfaces were observed to investigate the lesions of different degree in these specimens. The data were analyzed with SPSS20.0 software package. RESULTS: Surface roughness was group B> group A > group C, SBS was group B>group A>group C. CONCLUSIONS: Under the condition of 180℃, bonding strength between zirconia and resin cement after treatment with 20% NaOH solution was significantly higher than without any treatment, but lower than sand blasting treatment.

Key words: Zirconia ceramic, Hot alkali solution treatment, Surface roughness, Shear bond strengths

CLC Number:

R783.1

WAN Li-yang, ZHU Hong -shui. Experimental research of hot alkaline solution etching treatment on zirconia/resin bonding strength[J]. Shanghai Journal of Stomatology, 2017, 26(6): 590-593.

References

[1] 戴文雍, 印厚才, 陈晨, 等. 热酸溶液蚀刻对氧化锆粘接强度的影响 [J]. 华西口腔医学杂志, 2013, 31(6): 569-573.
[2] Su YS. Surface treatment of zirconia ceramic: United States, 4135012[P]. 1979-01-16.
[3] Casucci A, Mazzitelli C, Monticelli F, et al. Morphological analysis of three zirconium oxide ceramics: effect of surface treatments [J]. Dent Mater, 2010, 26(8): 751-760.
[4] Kumbuloglu O, Lassila LV, User A, et al. Bonding of resin composite luting cements to zirconium oxide by two air-particle abrasion methods [J]. Oper Dent, 2006, 31(2): 248-255.
[5] Gomes AL, Castillo-Oyague R, Lynch CD, et al. Influence of sandblasting granulometry and resin cement composition on microtensile bond strength to zirconia ceramic for dental prosthetic frameworks [J]. J Dent, 2013, 41(1): 31-41.
[6] Sato H, Yamada K, Pezzotti G, et al. Mechanical properties of dental zirconia ceramics changed with sandblasting and heat treatment [J]. Dent Mater J, 2008, 27(3): 408-414.
[7] 曾强, 李宁, 周亚男, 等. 氧化铝喷砂对牙科用氧化锆基底与饰面瓷结合强度的影响[J]. 华西口腔医学杂志, 2015, 33(6): 638-641.
[8] Tsukakoshi M, Shinya A, Gomi H, et al. Effects of dental adhesive cement and surface treatment on bond strength and leakage of zirconium oxide ceramics[J]. Dent Mater J, 2008, 27(2): 159-171.
[9] Zhang Y, Lawn BR, Malament KA, et al. Damage accumulation and fatigue life of particle-abraded ceramics[J]. Int J Prosthodont, 2006, 19(5): 442-448.
[10] 温宁, 伊元夫, 邵龙泉. 表面处理方法对牙科氧化锆陶瓷表面相结构及微观结构影响[J]. 稀有金属材料与工程, 2009, 38(S2): 848-851.
[11] Javid AH, Hasani AH, Golshan G. Selective removal of heavy metals from ferric chloride caused by etching processes by using sulfide precipitation[J]. J Environ Sci Technol, 2004, (20): 35-45.
[12] Casucci A, Osorio E, Osorio R, et al. Influence of different surface treatments on surface zirconia frameworks [J]. J Dent, 2009, 37(11): 891-897.
[13] Casucci A, Monticelli F, Goracci C, et al. Effect of surface pre-treatments on the zirconia ceramic-resin cement microtensile bond strength [J]. Dent Mater 2011, 27(10): 1024-1030.
[14] Ferrari M, Borracchini A, Bertelli E, et al. Evaluation of a chemical etching solution for nickel-chromium-beryllium and chromium-cobalt alloys [J]. J Prosth Dent, 1989, 62(5): 516-521.
[15] 吕品, 姜婷. 热酸蚀处理对氧化锆表面剪切粘接强度的影响 [J]. 北京大学学报(医学版), 2014, 46(2): 302-305.